Glass Fiber ABS
Eryone Glass Fiber ABS is a glass fiber reinforced ABS material that supports printing in
open environments. It features a balanced combination of strength, rigidity, and warping resistance, with a heat resistance temperature of up to 82°C. The printing speed can reach 150 mm/s, and it
has a matte, fine sand-smooth surface texture. It offers excellent mechanical properties, thermal
stability, and printing efficiency, making it suitable for 3D printing applications that require certain
levels of strength, rigidity, and heat resistance, such as tooling fixtures, manufacturing jigs, enclosures, and structural components. Note: The glass fiber content is 10%.
Part I： Suggests Printing Parameters
| Parameter | Set up |
| Nozzle temperature | 240-280 ℃ |
| Bed temperature | 80-100℃ |
| Bed materia | glass, PEI, spring steel plate |
| Bottom printing temperature | / |
| Sealed printing | Sealing print quality is better, supporting open printing |
| Printing speed | 30-150mm/s |
| Drying conditions | 60℃, 4h |
Part II： Physical Properties of Materials
| Property | Testing Method | Unit | Typical Value |
| Density(g/cm³ at 21.5 ° C） | ASTM D792 (ISO 1183, GB/T 1033) | g/cm³ | 1.1 |
| Vicat Softening Temperature(° C) | ASTM D1525 (ISO 306 GB/T 1633) | ℃ | / |
| Heat distortion temperature(° C) | ASTM D648 1.8MPa 0.45MPa | ℃ | 82 |
| Glass transition temperature (° C) | DSC, 10 ° C/min | ℃ | 104 |
| Melt Index(g/10 min) | 220 ° C, 10kg 240 ° C, 2.16 kg | g/10min | 30 |
Part III: Mechanical Properties of Printed Samples
| Property | Test conditions | Test standards | unit | Typical Value |
| Tensile strength X-Y | 50mm/min | GB/T 1040.4 | MPa | 37.2 |
| Elastic modulus X-Y | 50mm/min | GB/T 1040.1-2006 | MPa | 1735.8 |
| Elongation at break X-Y | 50mm/min | GB/T 1040.4 | % | 2.0 |
| Tensile strength X-Z | 50mm/min | GB/T 1843 | MPa | 19.2±4 |
| Elastic modulus X-Z | 50mm/min | GB/T 1040.1-2006 | MPa | 1651.2 |
| Elongation at break X-Z | 50mm/min | GB/T 1040.4 | % | 1.6 |
| Bending strength | 2mm/min | GB/T 9341 | MPa | 57.9 |
| Bending modulus | 2mm/min | GB/T 9341 | MPa | 2487.4 |
| Charpy Impact strenght | 2.75J | GB/T 1843 | kJ/m2 | 6.2 |
Note: All splines are printed under the following conditions: printing temperature=270 ° C, printing
speed=150mm/s, base plate 90° C, filling=100%, nozzle diameter=0.4mm