Hyper Speed Four colors Silk PLA
The Eryone High-Speed Silk PLA is a material with a thoroughly improved
formulation, offering significantly enhanced printing speeds compared to standard silk
PLA, reaching up to 500 mm/s. Additionally, its tensile strength has been notably
increased, with the Z-axis tensile strength reaching 20 MPa. This high-speed silk PLA
material delivers a more lustrous finish, presenting a silk-like appearance. The
brightness can be controlled by adjusting the temperature and speed: higher
temperatures and slower printing speeds result in increased brightness.
Part I: Suggests Printing Parameters
| Parameter | Set up |
| Nozzle temperature | 190℃-220℃ |
| Bed temperature | 55-70℃ |
| Bed material | glass, PEI, spring steel plate |
| Bottom printing temperature | 190℃-220℃ |
| Sealed printing | Open Printing/closed printing |
| Printing speed | 30-500mm/s |
| Drying conditions | 65℃-75℃，12H |
Part II: Physical Properties of Materials
| Property | Testing Method | Unit | Typical Value |
| Density(g/cm³ at 21.5 ° C） | ASTM D792 (ISO 1183, GB/T 1033) | g/cm³ | 1.32 |
| Vicat Softening Temperature(° C) | ASTM D1525 (ISO 306 GB/T 1633) | ℃ | 56 |
| Heat distortion temperature(° C | ASTM D648 1.8MPa 0.45MPa | ℃ | 50 |
| Glass transition temperature (° C) | DSC, 10 ° C/min | ℃ | 57 |
| Melt Index(g/10 min) | 220 ° C, 10kg 240 ° C, 2.16 kg | g/10min | 20±1.5 |
Part III: Mechanical Properties of Printed Samples
| Property | Test conditions | Test standards | unit | Typical Value |
| Tensile strength X-Y | 50mm/min | GB/T 1040.4 | MPa | 62.7 |
| Elastic modulus X-Y | 50mm/min | GB/T 1040.1-2006 | MPa | 1932.1 |
| Elongation at break X-Y | 50mm/min | GB/T 1040.4 | % | 2.3 |
| Tensile strength X-Z | 50mm/min | GB/T 1843 | MPa | 19.1 |
| Elastic modulus X-Z | 50mm/min | GB/T 1040.1-2006 | MPa | 1873.5 |
| Elongation at break X-Z | 50mm/min | GB/T 1040.4 | % | 1.9 |
| Bending strength | 2mm/min | GB/T 9341 | MPa | 86.7 |
| Bending modulus | 2mm/min | GB/T 9341 | MPa | 2917.3 |
| Charpy Impact strenght | 2.75J | GB/T 1843 | kJ/m2 | 3.8 |
Note: All splines are printed under the following conditions: printing temperature=215 ° C, printing speed=80mm/s, base plate 60 ° C, filling=100%, nozzle diameter=0.4mm
Disclaimers
The values given in this data table are for reference and comparison only. They
should not be used for design specifications or quality control. The actual value may
vary depending on the printing conditions. The final performance of printed
components depends not only on the material, but also on the component design, environmental conditions, printing conditions, and so on. Product specifications are
subject to change without prior notice.